The Effect of Chlorhexidine on Push-out Bond Strength of Mineral Trioxide Aggregate |
|
| چکیده فارسی مقاله |
Conclusions This study suggested that chlorhexidine had no negative effect on the bond strengths of MTA-treated dentin. Results There were no statistically significant differences between all the experimental groups. The mode of bond failure was predominantly mixed for distilled water groups and cohesive for CHX groups. Materials and Methods Sixty dentin disks with a thickness of 1.5 ± 0.2 mm and lumen size of 1.3 mm were prepared. Dentin disks were randomly divided into four groups (n = 15), and their lumens were filled with MTA mixed with distilled water (groups 1 and 3) or with chlorhexidine 2% (groups 2 and 4). Specimens were incubated at 37°C for 3 days (groups 1 and 2) or 21 days (groups 3 and 4). Bond strengths of the MTA-treated dentin surfaces were evaluated using a universal testing machine, and bond failure on the disks was examined by light microscope. Data was analyzed using Kruskal-Wallis H test (P = 0.976). Objectives The aim of this study was to evaluate the effect of chlorhexidine (2%) on push-out bond strength of Mineral Trioxide Aggregate (MTA). Background Trioxide Aggregate (MTA) has been widely used in root canal therapy. MTA has been mixed with chlorhexidine to increase its antimicrobial effect. |
|
| کلیدواژههای فارسی مقاله |
|
|
| عنوان انگلیسی |
The Effect of Chlorhexidine on Push-out Bond Strength of Mineral Trioxide Aggregate |
|
| چکیده انگلیسی مقاله |
Conclusions This study suggested that chlorhexidine had no negative effect on the bond strengths of MTA-treated dentin. Results There were no statistically significant differences between all the experimental groups. The mode of bond failure was predominantly mixed for distilled water groups and cohesive for CHX groups. Materials and Methods Sixty dentin disks with a thickness of 1.5 ± 0.2 mm and lumen size of 1.3 mm were prepared. Dentin disks were randomly divided into four groups (n = 15), and their lumens were filled with MTA mixed with distilled water (groups 1 and 3) or with chlorhexidine 2% (groups 2 and 4). Specimens were incubated at 37°C for 3 days (groups 1 and 2) or 21 days (groups 3 and 4). Bond strengths of the MTA-treated dentin surfaces were evaluated using a universal testing machine, and bond failure on the disks was examined by light microscope. Data was analyzed using Kruskal-Wallis H test (P = 0.976). Objectives The aim of this study was to evaluate the effect of chlorhexidine (2%) on push-out bond strength of Mineral Trioxide Aggregate (MTA). Background Trioxide Aggregate (MTA) has been widely used in root canal therapy. MTA has been mixed with chlorhexidine to increase its antimicrobial effect. |
|
| کلیدواژههای انگلیسی مقاله |
|
|
| نویسندگان مقاله |
علیرضا عدل | alireza adl
department of endodontic, school of dentistry, shiraz university of medical sciences, shiraz, ir iran
سازمان اصلی تایید شده: دانشگاه علوم پزشکی شیراز (Shiraz university of medical sciences)
نوشین سادات شجاعی | nooshin sadat shojaee
department of endodontic, school of dentistry, shiraz university of medical sciences, shiraz, ir iran; department of endodontic, school of dentistry, shiraz university of medical sciences, shiraz, ir iran. tel 98-7116263193, fax 98-7116270325
سازمان اصلی تایید شده: دانشگاه علوم پزشکی شیراز (Shiraz university of medical sciences)
فرشته صبح نمایان | fereshte sobhnamayan
department of endodontic, school of dentistry, shiraz university of medical sciences, shiraz, ir iran
سازمان اصلی تایید شده: دانشگاه علوم پزشکی شیراز (Shiraz university of medical sciences)
ندا سادات شجاعی | neda sadat shojaee
school of dentistry, shiraz university of medical sciences, shiraz, ir iran
سازمان اصلی تایید شده: دانشگاه علوم پزشکی شیراز (Shiraz university of medical sciences)
|
|
| نشانی اینترنتی |
http://www.avicennajdr.com/index.php?page=article&article_id=21195 |
| فایل مقاله |
فایلی برای مقاله ذخیره نشده است |
| کد مقاله (doi) |
10.17795/ajdr-21195 |
| زبان مقاله منتشر شده |
fa |
| موضوعات مقاله منتشر شده |
|
| نوع مقاله منتشر شده |
1 |
|
|
|
برگشت به:
صفحه اول پایگاه |
نسخه مرتبط |
نشریه مرتبط |
فهرست نشریات
|